Cu-FRHC (CW005A)
| Qib: | Cu-FRHC |
| Tus lej: | CWJ 005A |
| Kev faib tawm: | khob |
| Txheem: | TS EN 13601: 2002 Copper thiab tooj liab alloys Copper pas nrig, bar thiab xaim rau cov khoom siv hluav taws xob TS EN 13600: 2002 Copper thiab tooj liab alloys Seamless tooj liab raj rau hluav taws xob lub hom phiaj TS EN 13602: 2002 Copper thiab tooj liab alloys Kos, puag ncig tooj liab hlau rau kev tsim hluav taws xob conductors TS EN 1976: 1998 Copper thiab tooj liab alloys Casting unwrought tooj liab cov khoom TS EN 13599: 2002 Copper thiab tooj liab alloys Copper phaj, ntawv thiab sawb rau hluav taws xob lub hom phiaj TS EN 13605: 2002 Copper thiab tooj liab alloys tooj liab profiles thiab profiled hlau rau hluav taws xob lub hom phiaj |
| Qib sib npaug: | Mus ntawm no |
Tshuaj muaj pes tsawg leeg % ntawm qib Cu-FRHC (CW005A)
| Cu suav nrog Ag < {{0}}.015%; O <0.06% tso cai |
| Cu | O | Lwm tus |
| qis 99.9 | max 0.04 | tag nrho 0.04 |
Mechanical zog ntawm qib Cu-FRHC (CW005A)
| Rm- Tensile zog (MPa) (R200) | 200 |
| Rm- Tensile zog (MPa) (R250) | 250 |
| Rm- Tensile zog (MPa) (R350) | 350 |
| Rp0.20.2% pov thawj lub zog (MPa) (R200) | 120 |
| Rp0.20.2% pov thawj lub zog (MPa) (R250) | 180-200 |
| Rp0.20.2% pov thawj lub zog (MPa) (R350) | 320 |
| A- Min. elongation ntawm pob txha (%) (R200) | 35 |
| A- Min. elongation ntawm pob txha (%) (R250) | 12-15 |
| A- Min. elongation ntawm pob txha (%) (R350) | 5 |
| A- Min. elongation Lo=100mm (%) (R200) | 25 |
| A- Min. elongation Lo=100 hli (%) (R250) | 8 |
| A- Min. elongation Lo=100 hli (%) (R350) | 3 |
| Vickers hardness (HV): (H035) (R200) | 35 - 65 |
| Brinell hardness (HB): (H065) (R250) | 65 - 90 |
| Brinell hardness (HB): (H100) (R350) | 100 |
Cov cuab yeej Cu-FRHC
| Volume resistivity=0 01724 - 0.01786 Ω * mm² / m ; |
Qib sib npaug ntawm qib Cu-FRHC (CW005A)
Ceeb toom! Tsuas yog siv tau
| EU EN |
Lub teb chaws Yelemees DIN, NWS |
||
| Cu-FRHC |
|
Casting txheej txheem
| GS | Xuab zeb casting |
| GM | Permanent pwm casting |
| GZ | Centrifugal casting |
| GC | Nruam casting |
| GP | Siab tuag casting |
Khoom siv
| R | Cov khoom siv los ntawm qhov tsawg kawg nkaus tus nqi ntawm tensile lub zog yuav tsum tau rau cov khoom uas yuav tsum tau tensile zog thiab elongation yuav tsum tau |
| H | Cov khoom siv raws li qhov tsawg kawg nkaus tus nqi ntawm hardness yuav tsum tau rau cov khoom uas yuav tsum tau hardness yuav tsum tau |
Mechanical zog
| ReH | Yam tsawg kawg nkaus yield zog / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Tensile zog / Zugfestigkeit / Resistance a la traction |
| A | Tsawg kawg elongation / Mindestwert der Bruchdehnung / Allongement tsawg |
| J | Kev ntsuas qhov cuam tshuam / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
Cu-FRHC (CW005A) Cupper |