CuSn11P-B (CB481K)
| Qib: | CuSn11P-B |
| Tus lej: | wb 481k |
| Kev faib tawm: | Tooj-tin alloy |
| Txheem: | TS EN 1982: 2008 Copper thiab tooj liab alloys Ingots thiab castings |
| Qib sib npaug: | Tsis muaj ntaub ntawv |
Tshuaj muaj pes tsawg leeg % ntawm qib CuSn11P-B (CB481K)
| Lub ntsiab lus -B yog ntxiv rau lub npe los txheeb xyuas cov khoom hauv daim ntawv ntawm ingots |
| Fe | Si | Mn | Ni | P | S | Al | Cu | Pb | Zn | Sb | Sn |
| max 0.1 | max 0.01 | max 0.05 | max 0.1 | 0.6 - 1 | max 0.05 | max 0.01 | 87 - 89.3 | max 0.25 | max 0.05 | max 0.05 | 10.2 - 11.5 |
Mechanical zog ntawm qib CuSn11P-B (CB481K)
| Rm- Tensile zog (MPa) (GS) | 250 |
| Rm- Tensile zog (MPa) (GM) | 310 |
| Rm- Tensile zog (MPa) (GC) | 350 |
| Rm- Tensile zog (MPa) (GZ) | 330 |
| Rp0.20.2% pov thawj lub zog (MPa) (GS) | 130 |
| Rp0.20.2% pov thawj lub zog (MPa) (GM) | 170 |
| Rp0.20.2% pov thawj lub zog (MPa) (GC) | 170 |
| Rp0.20.2% pov thawj lub zog (MPa) (GZ) | 170 |
| A- Min. elongation ntawm pob txha (%) (GS) | 5 |
| A- Min. elongation ntawm pob txha (%) (GM) | 2 |
| A- Min. elongation ntawm pob txha (%) (GC) | 5 |
| A- Min. elongation ntawm pob txha (%) (GZ) | 4 |
| Brinell hardness (HBW): (GS) | 60 |
| Brinell hardness (HBW): (GM) lossis (GC) lossis (GZ) | 85 |
Casting txheej txheem
| GS | Xuab zeb casting |
| GM | Permanent pwm casting |
| GZ | Centrifugal casting |
| GC | Nruam casting |
| GP | Siab tuag casting |
Khoom siv
| R | Cov khoom siv los ntawm qhov tsawg kawg nkaus tus nqi ntawm tensile lub zog yuav tsum tau rau cov khoom uas yuav tsum tau tensile zog thiab elongation yuav tsum tau |
| H | Cov khoom siv raws li qhov tsawg kawg nkaus tus nqi ntawm hardness yuav tsum tau rau cov khoom uas yuav tsum tau hardness yuav tsum tau |
Mechanical zog
| ReH | Yam tsawg kawg nkaus yield zog / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Tensile zog / Zugfestigkeit / Resistance a la traction |
| A | Tsawg kawg elongation / Mindestwert der Bruchdehnung / Allongement tsawg |
| J | Kev ntsuas qhov cuam tshuam / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuSn11P-B (CB481K) tooj liab-tin alloy |