CuZn0.5 (CW119C)
| Qib: | CuZn0.5 |
| Tus lej: | CWJ 119C |
| Kev faib tawm: | Cupper alloy |
| Qhov ntom | 8.9 g / cm³ |
| Txheem: | TS EN 1652: 1998 Copper thiab tooj liab alloys Phaj, ntawv, sawb thiab voj voog rau kev siv dav dav TS EN 1172: 1997 Copper thiab tooj liab alloys Daim ntawv thiab sawb rau lub tsev TS EN 13148: 2001 Copper thiab tooj liab alloys Kub-dip tinned strip |
| Qib sib npaug: | Mus ntawm no |
Tshuaj muaj pes tsawg leeg % ntawm qib CuZn0.5 (CW119C)
| P | Zn | Lwm tus | - |
| max 0.02 | 0.1 - 1 | tag nrho 0.1 | Cu - seem |
Mechanical zog ntawm qib CuZn0.5 (CW119C)
| Rm- Tensile zog (MPa) (R220) | 220-260 |
| Rm- Tensile zog (MPa) (R240) | 240-300 |
| Rm- Tensile zog (MPa) (R290) | 290-360 |
| Rp0.20.2% pov thawj lub zog (MPa) (R220) | 140 |
| Rp0.20.2% pov thawj lub zog (MPa) (R240) | 180 |
| Rp0.20.2% pov thawj lub zog (MPa) (R290) | 250 |
| A- Min. elongation ntawm pob txha (%) (R220) | 42 |
| A- Min. elongation ntawm pob txha (%) (R240) | 15 |
| A- Min. elongation ntawm pob txha (%) (R290) | 6 |
| A- Min. elongation Lo=50 hli (%) (R220) | 33 |
| A- Min. elongation Lo=50 hli (%) (R240) | 8 |
| Vickers hardness (HV): (H040) | 40 - 65 |
| Vickers hardness (HV): (H065) | 65 - 95 |
| Vickers hardness (HV): (H085) | 85 - 115 |
Qib sib npaug ntawm qib CuZn0.5 (CW119C)
Ceeb toom! Tsuas yog siv tau
| EU EN |
Lub teb chaws Yelemees DIN, NWS |
||
| CuZn0.5 |
|
Casting txheej txheem
| GS | Xuab zeb casting |
| GM | Permanent pwm casting |
| GZ | Centrifugal casting |
| GC | Nruam casting |
| GP | Siab tuag casting |
Khoom siv
| R | Cov khoom siv los ntawm qhov tsawg kawg nkaus tus nqi ntawm tensile lub zog yuav tsum tau rau cov khoom uas yuav tsum tau tensile zog thiab elongation yuav tsum tau |
| H | Cov khoom siv raws li qhov tsawg kawg nkaus tus nqi ntawm hardness yuav tsum tau rau cov khoom uas yuav tsum tau hardness yuav tsum tau |
Mechanical zog
| ReH | Yam tsawg kawg nkaus yield zog / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Tensile zog / Zugfestigkeit / Resistance a la traction |
| A | Tsawg kawg elongation / Mindestwert der Bruchdehnung / Allongement tsawg |
| J | Kev ntsuas qhov cuam tshuam / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn{0}}.5 (CW119C) Cupper alloy |