| Qib: | Cu-DHP |
| Tus lej: | qw 024a |
| Kev faib tawm: | Phosphorus-muaj tooj liab qib |
| Qhov ntom | 8.9 g / cm³ |
| Txheem: | TS EN 1652: 1998 Copper thiab tooj liab alloys Phaj, ntawv, sawb thiab voj voog rau kev siv dav dav TS EN 1653: 1998 Copper thiab tooj liab alloys Phaj, daim ntawv thiab lub voj voog rau boilers, cov hlab ntsha siab thiab cov chav dej kub cia TS EN 1976: 1998 Copper thiab tooj liab alloys Casting unwrought tooj liab cov khoom TS EN 12163: 1998 Copper thiab tooj liab alloys Qws rau lub hom phiaj dav dav TS EN 12166: 1998 Copper thiab tooj liab alloys Hlau rau lub hom phiaj dav dav TS EN 12167: 1998 Copper thiab tooj liab alloys Profiles thiab rectangular bar rau dav siv TS EN 1172: 1997 Copper thiab tooj liab alloys Daim ntawv thiab sawb rau lub tsev TS EN 12165: 1998 Copper thiab tooj liab alloys Wrought thiab unwrought forging Tshuag TS EN 12451: 1999 Copper thiab tooj liab alloys Seamless, round tubes rau cua sov exchangers TS EN 12452: 1999 Copper thiab tooj liab alloys Rolled, finned, seamless raj rau tshav kub exchangers TS EN 12449: 1999 Copper thiab tooj liab alloys Seamless, round raj rau lub hom phiaj dav dav TS EN 12420: 1999 Copper thiab tooj liab alloys Forgings TS EN 13148: 2001 Copper thiab tooj liab alloys Kub-dip tinned strip |
| Qib sib npaug: | Mus ntawm no |
Cov tshuaj muaj pes tsawg leeg % ntawm qib Cu-DHP (CW024A)
| Cu suav nrog Ag < 0.015% |
| P | Cu |
| 0.015 - 0.04 | qis 99.9 |
Mechanical zog ntawm qib Cu-DHP (CW024A)
| Rm- Tensile zog (MPa) (R220) | 220-260 |
| Rm- Tensile zog (MPa) (R240) | 240-300 |
| Rm- Tensile zog (MPa) (R290) | 290-360 |
| Rm- Tensile zog (MPa) (R200) | 200-250 |
| Rp0.20.2% pov thawj lub zog (MPa) (R220) | 140 |
| Rp0.20.2% pov thawj lub zog (MPa) (R240) | 180 |
| Rp0.20.2% pov thawj lub zog (MPa) (R290) | 250 |
| Rp0.20.2% pov thawj lub zog (MPa) (R200) | 40-100 |
| A- Min. elongation ntawm pob txha (%) (R240) | 15 |
| A- Min. elongation ntawm pob txha (%) (R290) | 6 |
| A- Min. elongation ntawm pob txha (%) (R200) | 33-42 |
| A- Min. elongation Lo=50 hli (%) (R220) | 33 |
| A- Min. elongation Lo=50 hli (%) (R240) | 8 |
| A- Min. elongation Lo=50 hli (%) (R290) | 4 |
| Vickers hardness (HV): (H065) | 65 - 95 |
| Vickers hardness (HV): (H090) | 90 - 110 |
| Vickers hardness (HV): (H040) | 40 - 65 |
Qib sib npaug ntawm qib Cu-DHP (CW024A)
Ceeb toom! Tsuas yog siv tau
| EU EN |
Lub teb chaws Yelemees DIN, NWS |
Russia GOST |
|||
| Cu-DHP |
|
|
Casting txheej txheem
| GS | Xuab zeb casting |
| GM | Permanent pwm casting |
| GZ | Centrifugal casting |
| GC | Nruam casting |
| GP | Siab tuag casting |
Khoom siv
| R | Cov khoom siv los ntawm qhov tsawg kawg nkaus tus nqi ntawm tensile zog yuav tsum tau rau cov khoom uas yuav tsum tau tensile zog thiab elongation yuav tsum tau |
| H | Cov khoom siv raws li qhov tsawg kawg nkaus tus nqi ntawm hardness yuav tsum tau rau cov khoom uas yuav tsum tau hardness yuav tsum tau |
Mechanical zog
| ReH | Yam tsawg kawg nkaus yield zog / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Tensile zog / Zugfestigkeit / Resistance a la traction |
| A | Tsawg kawg elongation / Mindestwert der Bruchdehnung / Allongement tsawg |
| J | Kev ntsuas qhov cuam tshuam / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
Cu-DHP (CW024A) phosphorus-muaj tooj liab qib |