CuMn11Al8Fe3Ni3-C (CC212E)
| Qib: | CuMn11Al8Fe3Ni3-C |
| Tus lej: | TIAB SA 212E |
| Kev faib tawm: | Copper-manganese-aluminium alloy |
| Txheem: | TS EN 1982: 2008 Copper thiab tooj liab alloys Ingots thiab castings |
| Qib sib npaug: | Tsis muaj ntaub ntawv |
Tshuaj muaj pes tsawg leeg % ntawm qib CuMn11Al8Fe3Ni3-C (CC212E)
| Lub ntsiab lus -C yog ntxiv rau lub npe los txheeb xyuas cov khoom hauv daim ntawv ntawm castings |
| Fe | Si | Mn | Ni | Al | Cu | Pb | Mg | Zn | Sn |
| 2 - 4 | max 0.1 | 8 - 15 | 1.5 - 4.5 | 7 - 9 | 68 - 77 | max 0.05 | max 0.05 | max 1.7 Nws | max 0.5 |
Mechanical zog ntawm qib CuMn11Al8Fe3Ni3-C (CC212E)
| Rm- Tensile zog (MPa) (GS) | 630 |
| Rp0.20.2% pov thawj lub zog (MPa) (GS) | 275 |
| A- Min. elongation ntawm pob txha (%) (GS) | 18 |
| Brinell hardness (HBW): (GS) | 150 |
Casting txheej txheem
| GS | Xuab zeb casting |
| GM | Permanent pwm casting |
| GZ | Centrifugal casting |
| GC | Nruam casting |
| GP | Siab tuag casting |
Khoom siv
| R | Cov khoom siv los ntawm qhov tsawg kawg nkaus tus nqi ntawm tensile lub zog yuav tsum tau rau cov khoom uas yuav tsum tau tensile zog thiab elongation yuav tsum tau |
| H | Cov khoom siv raws li qhov tsawg kawg nkaus tus nqi ntawm hardness yuav tsum tau rau cov khoom uas yuav tsum tau hardness yuav tsum tau |
Mechanical zog
| ReH | Yam tsawg kawg nkaus yield zog / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Tensile zog / Zugfestigkeit / Resistance a la traction |
| A | Tsawg kawg elongation / Mindestwert der Bruchdehnung / Allongement tsawg |
| J | Kev ntsuas qhov cuam tshuam / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuMn11Al8Fe3Ni 3-C (CC212E) Copper-manganese-aluminium alloy |