CuNi1P (CW 108C)
| Qib: | CuNi 1 P |
| Tus lej: | CWJ 108C |
| Kev faib tawm: | Tsawg alloyed tooj liab alloy |
| Txheem: | TS EN 12163: 1998 Copper thiab tooj liab alloys Qws rau lub hom phiaj dav dav |
| Qib sib npaug: | Tsis muaj ntaub ntawv |
Tshuaj muaj pes tsawg leeg % ntawm qib CuNi1P (CW108C)
| Ni | P | Lwm tus | - |
| 0.8 - 1.2 | 0.15 - 0.25 | tag nrho 0.1 | Cu - seem |
Mechanical zog ntawm qib CuNi1P (CW108C)
| Rm- Tensile zog (MPa) (R250) | 250 |
| Rm- Tensile zog (MPa) (R400) | 400 |
| Rm- Tensile zog (MPa) (R650) | 650 |
| Rm- Tensile zog (MPa) (R700) | 700 |
| Rp0.20.2% pov thawj lub zog (MPa) (R250) | 140 |
| Rp0.20.2% pov thawj lub zog (MPa) (R400) | 330 |
| Rp0.20.2% pov thawj lub zog (MPa) (R650) | 500 |
| Rp0.20.2% pov thawj lub zog (MPa) (R700) | 630 |
| A- Min. elongation ntawm pob txha (%) (R250) | 25 |
| A- Min. elongation ntawm pob txha (%) (R400) | 10 |
| A- Min. elongation ntawm pob txha (%) (R700) | 7 |
| Vickers hardness (HV): (H065) | 70 - 100 |
| Vickers hardness (HV): (H110) | 115 - 165 |
| Vickers hardness (HV): (H200) | 210 |
Casting txheej txheem
| GS | Xuab zeb casting |
| GM | Permanent pwm casting |
| GZ | Centrifugal casting |
| GC | Nruam casting |
| GP | Siab tuag casting |
Khoom siv
| R | Cov khoom siv los ntawm qhov tsawg kawg nkaus tus nqi ntawm tensile zog yuav tsum tau rau cov khoom uas yuav tsum tau tensile zog thiab elongation yuav tsum tau |
| H | Cov khoom siv raws li qhov tsawg kawg nkaus tus nqi ntawm hardness yuav tsum tau rau cov khoom uas yuav tsum tau hardness yuav tsum tau |
Mechanical zog
| ReH | Yam tsawg kawg nkaus yield zog / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Tensile zog / Zugfestigkeit / Resistance a la traction |
| A | Tsawg kawg elongation / Mindestwert der Bruchdehnung / Allongement tsawg |
| J | Kev ntsuas qhov cuam tshuam / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuNi1P (CW108C) Tsawg alloyed tooj liab alloy |